Timeplast
TimeMass Fire
PVA1.75 mm
Composition / filler: Proprietary Timeplast/TimeMass matrix: in-house polymerized alcohols with ~70 % structured water (water-soluble), plus the functional additive named below.
Print parameters
| Diameter | 1.75 mm |
|---|---|
| Nozzle | 230–245 °C |
| Bed | 75 °C |
| Speed | 60–120 mm/s |
| Fan | — |
| Drying (temp / time) | 68 °C / 2 h |
| Density | — |
Mechanical & thermal properties
| Tensile strength | –MPa |
|---|---|
| Tensile modulus | –MPa |
| Elongation at break | –% |
| Flexural strength | –MPa |
| Impact strength | –kJ/m² |
| Hardness | — |
| HDT (heat deflection) | –°C |
| Glass transition (Tg) | — |
| VICAT | –°C |